Table of Content
15 5 PH Stainless Steel Fasteners Chemical Compatibility
| Grade | C | Ni | Si | Mo | Mn | P + S Max | Cr | Cu | |
| SS 15-5PH | max. | 0.07 | 4.50 | 1.00 | 0.50 | 1.0 | 0.015S | 15.50 | 4.50 |
| min. | - | 3.50 | - | - | - | 0.03P | 14.00 | 2.50 | |
Equivalent Grades of 15-5PH Nuts
| MATERIAL | UNS | WERKSTOFF NR. |
| 15-5 PH | S15500 | 1.4545 |
UNS S15500 Studs Mechanical Strength Table
| Grade | Tensile Strength (ksi) min | Yield Strength 0.2% Proof (ksi) min | Hardness | Elongation (% in 50mm) min |
| 15 5 PH | 190 | 170 | 388 | 10 |
15-5PH Bolts Specification and Material Grade
| Available Lengths | From 3 - 200 mm |
| Specification | ASTM F2281, B564 / ASME SB564, SF2281 |
| Sizes Range | M02 – M160 | 3/6" upto 2" |
| In Form of: |
|
|---|---|
| Threads | METRIC, UNC, BSW, BSF, UNF or as required |
15-5PH Bolts Applications
- Power Generation
- Off-Shore Oil Drilling Companies
- Gas Processing
- Petrochemicals
- Pharmaceuticals
- Specialty Chemicals
- Chemical Equipment
- Pharmaceutical Equipment
- Heat Exchangers
- Sea Water Equipment
- Pulp and Paper Industry
- Condensers
Stainless Steel Alloy 15-5 PH Nuts Physical Properties
| (J/kg.K) Specific Heat 0 to 100°C | (nW.m) Electrical Resistivity | (GPa) Elastic Modulus | (mm/m/°C) Mean Coeff. of Thermal Expansion | (kg/m3)Density | (W/m.K)Thermal Conductivity | |||
|---|---|---|---|---|---|---|---|---|
| – | – | – | 0-315°C | 0-100°C | 0-538°C | – | at 500°C | at 100°C |
| 460 | 600 | 200 | 11.0 | 10.4 | 11.4 | -7750 | 26.0 | 23.9 |
Surface Treatments of 15-5 PH Fasteners
- Electro Cadmium Plated Fasteners
- Aluminium Coated Fasteners
- Geomet Fasteners
- Zinc Coated Fasteners
- Teflon Coated Fasteners
- Zinc/Nickel by Electrodeposition Fasteners
- Xylon Coated Fasteners
- Phosphate Coated Fasteners
- Silver Coated Fasteners
- Hot Dipped Galvanized Fasteners
- Electro Zinc plated Fasteners
- Dacromet Fasteners
- Ceramic Filled PTFE Coated Fasteners
- Cadmium Coated Fasteners
- Electroless Nickel Plated Fasteners
- Zinc Nickel Coated Fasteners